Elastic rail clips are used to fasten rails together with concrete sleepers to the underlying base plate. Our rail clips are usually hot forged from forged spring steel.
The rail clips produced by Kingrail Parts can comply with UIC, BS, JIS and other standards. We can also customize rail clips according to customer specifications and requirements.
Specification:
Series | Type | Hardness | Material | Fatigue life | Surface |
E rail clip | E1,E2,E3 | 44-48HRC |
60Si2MnA: C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 60Si2CrA: C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 55Si2Mn: C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 38Si7: C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
For Dia.18 is 3 millions cycles without breaking. For Dia.20 is 5 millions cycles without breaking. |
Plain (oiled), Oxide black, color painting or upon customer requirement. |
E1609 | |||||
E1809 | |||||
E1817 | |||||
E2001 | |||||
E2006 | |||||
E2009 | |||||
E2055 | |||||
E2056 | |||||
Vossloh clip& Forged rail clip |
SKL1 | 42-47HRC | |||
PR rail clip | PR309 | 44-48HRC | |||
PR401 | |||||
PR601 | |||||
PR85 | |||||
We can also manufacture customized rail clips following your drawings or samples! |
Item | Materials | Diameter | Weight | HRC | Under pressure | Fatigue test | Export area |
Type III | 60Si2MnA | ø18 | 0.80kg | 44-48 | ≥950kgf |
5000000 times without breaking |
America Spain Brazil |
1809 | 60Si2MnA | ø18 | 0.63 kg | 44-48 | ≥950kgf | Southeast Asia | |
e1609 | 60Si2MnA | ø16 | 0.43 kg | 44-48 | ≥950kgf | America European | |
e1813 | 60Si2MnA | ø18 | 0.60 kg | 44-48 | ≥950kgf | America Brazil | |
e2001 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | Indonesia | |
e2007 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | Korea | |
e2009 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | European Brazil | |
e2055 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | America | |
e2056 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | Brazil Indonesia | |
e2063 | 60Si2MnA | ø20 | 0.80 kg | 44-48 | ≥950kgf | America UK | |
PR401 | 60Si2MnA | ø20 | 0.97 kg | 44-48 | ≥950kgf | America | |
PR415 | 60Si2MnA | ø20 | 0.95 kg | 44-48 | ≥950kgf | America Indonesia | |
PR601A | 60Si2MnA | ø22 | 1.23 kg | 44-48 | ≥950kgf | America Taiwan | |
SKL-1 | 38Si7 | ø13 | 0.53 kg | 44-48 | ≥950kgf | America Taiwan | |
SKL-3 | 38Si7 | ø13 | 0.53 kg | 44-48 | ≥950kgf | America Hong Kong |
Item No. | Material | Clip Lenth | Clip Hight | Clip Diameter | Hardness | Pressure | Fatigue test |
e2007 | 60Si2MnA | 105±5 | 38max | ø20±0.3 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
D1 | 60Si2MnA | 100±3 | 58±3.0 | ø18±0.25 | 44-48 | ≥8.25KN | 5,000,000 times without broken |
E18 | 60Si2MnA | 100±3 | 58±3.0 | ø18±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
E18 Anti-theft | 60Si2MnA | 100±3 | 57±3.0 | ø18±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
E19 | 60Si2MnA | 100±3 | 56.5±3.0 | ø20±0.25 | 44-48 | ≥8.25KN | 5,000,000 times without broken |
E20 | 60Si2MnA | 100±3 | 56.5±3.0 | ø20±0.25 | 44-48 | ≥8.25KN | 5,000,000 times without broken |
e1609 | 60Si2MnA | 93±3 | 30max | ø16±0.25 | 44-48 | ≥6.0KN | 5,000,000 times without broken |
e1809 | 60Si2MnA | 104±3 | 36max | ø18±0.25 | 44-48 | ≥7.5KN | 3,000,000 times without broken |
e1817 | 60Si2MnA | 104±3 | 37.5±3.0 | ø18±0.25 | 44-48 | ≥7.5KN | 5,000,000 times without broken |
e2009 | 60Si2MnA | 106±3 | ≤37.5 | ø20±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
e2039 | 60Si2MnA | 104±3 | 37max | ø20±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
e2055-1 | 60Si2MnA | 106±3 | 39±2.0 | ø20±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
e2055-2 | 60Si2MnA | 106±3 | 56.6±3.0 | ø20±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
e2055 | 60Si2MnA | 106±3 | 56.6±3.0 | ø20±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken |
e2056 | 60Si2MnA | 106±3 | 56.6±2.5 | ø20±0.25 | 44-48 | ≥2.7KN | 5,000,000 times without broken |
e2063 | 60Si2MnA | 110.5 | 53.4 | ø20±0.25 | 44-48 | ≥2.75KN | 5,000,000 times without broken |
III | 60Si2MnA | 110±2.8 | 63±2.8 | ø20±0.25 | 44-48 | 12.4-13KN | 5,000,000 times without broken |
PR85 | 60Si2MnA | 88±3 | ø13±0.25 | 44-48 | ≥9.5KN | 5,000,000 times without broken | |
PR309 | 60Si2MnA | 110 | ø19±0.25 | 44-48 | 700-900KN | 5,000,000 times without broken | |
PR401 | 60Si2MnA | 127±3 | 38.1±3.0 | ø20±0.3 | 44-48 | 5.0-7.0KN | 5,000,000 times without broken |
SKL-14 | 60Si2MnA | 155±2.0 | ø14±0.2 | 42-47 | ≥8.5KN | 5,000,000 times without broken | |
SKL-3 | 60Si2CrA | 120±2.0 | ø13±0.3 | 42-47 | 8-12KN | 5,000,000 times without broken | |
SKL-1 | 60Si3CrA | 133±2.0 | ø13±0.3 | 42-47 | 8-12KN | 5,000,000 times without broken |
Manufacturing process:
1. Raw material 2. Shearing 3. Heating to forging temperature 4. Forming 5. Quenching 6. Tempering 7. Surface treatment 8. Inspection and packaging